MOSFET with super-steep retrograded island

ABSTRACT

The present invention comprises a method for forming a semiconducting device including the steps of providing a layered structure including a substrate, a low diffusivity layer of a first-conductivity dopant; and a channel layer; forming a gate stack atop a protected surface of the channel layer; etching the layered structure selective to the gate stack to expose a surface of the substrate, where a remaining portion of the low diffusivity layer provides a retrograded island substantially aligned to the gate stack having a first dopant concentration to reduce short-channel effects without increasing leakage; growing a Si-containing material atop the recessed surface of the substrate; and doping the Si-containing material with a second-conductivity dopant at a second dopant concentration. The low diffusivity layer may be Si 1-x-y Ge x Z y , where Z can be carbon (C), xenon (Xe), germanium (Ge), krypton (Kr), argon (Ar), nitrogen (N), or combinations thereof.

RELATED APPLICATION

This application is a divisional of U.S. patent application Ser. No.10/954,838, filed Sep. 30, 2004.

FIELD OF THE INVENTION

The present invention relates to semiconductor devices and methods ofmanufacture, and more particularly to a method for manufacturing animproved metal oxide semiconductor (MOS) transistor having a steepretrograded dopant island.

BACKGROUND OF THE INVENTION

Field effect transistors (FETs) are the basic building block of today'sintegrated circuits (ICs). Such transistors can be formed inconventional bulk semiconductor substrates (such as silicon) or in anSOI layer of a silicon-on-insulator (SOI) substrate.

In order to be able to make ICs, such as memory, logic, and otherdevices, of higher integration density than currently feasible, one hasto find ways to further downscale the dimensions of field effecttransistors (FETs), such as metal-oxide-semiconductor field effecttransistors (MOSFETs) and complementary metal oxide semiconductors(CMOS). Scaling achieves compactness and improves operating performancein devices by shrinking the overall dimensions and operating voltages ofthe device, while maintaining the device's electrical properties.Additionally, all dimensions of the device must be scaled simultaneouslyin order to optimize the devices' electrical performance.

The scaling of the physical processes breaks down when new phenomena,which are typically absent in the larger structures, dominate thedevices behavior. For example, on decreasing the size of a MOSFET, atsome point the channel length approaches the depletion layer widths ofthe source and drain. This results in a degradation of the subthresholdcharacteristics of the device and a failure to achieve currentsaturation, which ultimately reduces control of the gate. Thisphenomenon is called the “short-channel effect”. Short-channel effectsare well known to those skilled in the art as the decrease in thresholdvoltage, Vt, in short-channel devices, i.e., sub-0.1 μm due to twodimensional electrostatic charge sharing between the gate and thesource/drain regions. One can suppress the short-channel effect byhighly doping the channel, at the expense of reduced mobility, loweroperating speed and increased risk for avalanches at the drain.

Prior attempts to improve short-channel effects include formingretrograded wells by implanting a high concentration of counter-dopantat the channel and source/drain extensions. The high concentration ofcounter-dopant at the PN junctions (source/channel interface,channel/drain interface) of the device disadvantageously result inincreased device leakage.

In view of the state of the art mentioned above, it would be highlydesirable to provide MOSFETS having gate lengths on the order of about100 nm or less, which overcome the above-described disadvantages.

SUMMARY OF THE INVENTION

One object of the present invention is to provide a MOSFET device, and amethod of forming thereof, having a steep retrograded dopant island, inwhich the steep retrograded dopant island is located underlying thedevice channel and effectively reduces the incidence of short-channeleffects. It is another object of the present invention to provide asteep retrograded dopant island that is substantially aligned to thesidewalls of the overlying gate region. It is a further object of thepresent invention to integrate the steep retrograded dopant island withstrained-Si device improvements. The term “steep retrograded dopantisland” denotes a doped region underlying the device channel of aMOSFET, in which the edge of the dopant region is substantially alignedto the sidewalls of the overlying gate region.

These and other objects and advantages are achieved in the presentinvention by a method that reduces the diffusion of the steepretrograded island dopant, so that the dopant is contained beneath andsubstantially aligned with the sidewall of the gate region. Morespecifically, the present invention reduces the diffusion of theretrograded island dopant by reducing the formation of dislocations inthe steep retrograded dopant island.

One aspect of the present invention relates to a method of forming aMOSFET having a steep retrograded dopant island, in which theretrograded dopant island is positioned substantially aligned with thegate region and has a dopant concentration to reduce the incidence ofshort-channel effects without increasing device leakage. Broadly, themethod of the present invention comprises the steps of:

providing a layered structure comprising a substrate, a low diffusivitylayer of a first conductivity type dopant atop said substrate, and achannel layer atop said low diffusivity layer of said first conductivitytype dopant;

forming a gate region atop a protected surface of said channel layer ofsaid layered structure;

etching said layered structure selective to said gate region to expose asurface of said substrate, where a remaining portion of said lowdiffusivity layer of said first conductivity type dopant provides aretrograded island substantially aligned with said gate region saidretrograded dopant island having a first dopant concentration to reduceshort-channel effects without increasing device leakage;

growing a Si-containing material atop said recessed surface of saidsubstrate;

forming offset spacers abutting said gate region; and

doping said Si-containing material with a second conductivity typedopant at a second dopant concentration.

The phrase “reduce short-channel effects without increasing deviceleakage” denotes that the present MOSFET comprising a steep retrogradeddopant island has less than ⅓ the leakage of a conventional transistor,since the contact area between the steep retrograded dopant island andthe source drain regions (i.e. source/drain extension regions and deepsource/drain regions) is substantially minimized. Therefore, since thecontact area between the steep retrograded dopant island and thesource/drain regions is minimized, short-channel effects may besubstantially reduced without incurring an increase in device leakage.

In accordance with the present method, the low diffusivity layercomprises S_(1-x-y)Ge_(x)Z_(y), wherein Z is a diffusion inhibitingdopant, x ranges from about 0.0 to about 0.2, and y ranges from about0.001 to about 0.01. The first conductivity type dopant can be a p-typedopant and the second conductivity dopant can be an n-type dopant.Alternatively, the first conductivity type dopant can be an n-typedopant and the second conductivity dopant can be a p-type dopant. Thediffusion inhibiting dopant may comprise carbon (C), xenon, (Xe)germanium (Ge), krypton (Kr), argon (Ar), nitrogen (N), or combinationsthereof.

The layered structure may be etched by a directional etch process usingthe overlying gate region as an etch mask. The etch process continuesthrough the exposed portions of the channel layer and the lowdiffusivity layer into the substrate until the upper surface of thesubstrate is recessed about 20 nm to about 100 nm from the substrate'soriginal upper surface. Following etching, the remaining portion of thelow diffusivity layer provides a steep retrograded island havingsidewalls that are substantially aligned to the sidewall of theoverlying gate region. The dopant concentration in the retrogradeddopant island is sufficient to reduce the incidence of short-channeleffects, yet does not increase device leakage. The presence of thediffusion inhibiting dopant within the retrograded dopant island ensuresthat the retrograded island dopant does not substantially diffuse beyondthe sidewalls of the overlying gate region.

Following etching, a Si-containing material is then epitaxially formedatop the exposed surface of the substrate. Epitaxially growing SiGe atopthe exposed surface of the substrate transfers a compressive stress tothe channel layer, while epitaxially growing Si:C atop the exposedsurface of the substrate transfers a tensile stress to the channellayer. The term “Si:C” denotes an epitaxially grown Si material that hasbeen doped with C, wherein the concentration of carbon ranges from1×10¹⁹ atoms/cm³ to 5×10²⁰ atoms/cm³.

Another aspect of the present invention relates to a MOSFET device,produced by the above method, in which a steep retrograded dopant islandreduces the incidence of the short-channel effects without increasingdevice leakage. In broad terms, the MOSFET comprises:

a gate region positioned on a channel portion of a substrate,

said channel portion of said substrate positioned atop a firstconductivity type retrograded dopant island and between a set of secondconductivity type doped regions; and

the first conductivity type retrograded dopant island substantiallyaligned to sidewalls of the gate region and having a first dopingconcentration sufficient to substantially reduce short-channel effectswithout increasing device leakage.

The channel portion of said substrate comprises a thickness ranging fromabout 10 nm to about 20 nm and a channel length of approximately 100 nmor less. The retrograded island has a doping concentration at least anorder of magnitude greater than said channel region. The inventiveMOSFET may further comprise deep source/drain regions, wherein the deepsource/drain regions are separated from the first conductivity typeretrograded dopant island by a leakage inhibiting dopant region. Theleakage inhibiting dopant region may have a first conductivity typedopant in a concentration of at least one order of magnitude less thanthe first conductivity type retrograded dopant island.

Another aspect of the present invention is an integrated circuitcomprising at least one semiconducting device comprising a gate regionpositioned on a channel portion of a substrate, said channel portion ofsaid substrate positioned atop a first conductivity type retrogradeddopant island and between a set of second conductivity type dopedextension regions, said first conductivity type retrograded dopantisland being substantially aligned to said gate region and having adoping concentration that substantially reduces short-channel effectswithin said at least one semiconducting device without increasing deviceleakage, and electrical contact to said at least one semiconductingdevice.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a pictorial representation (through a cross section view) ofthe inventive MOSFET device, in which a steep retrograded island reducesthe incidence of short-channel effects without increasing deviceleakage.

FIGS. 2-7 are pictorial representations (through a cross section view)of the present invention.

DETAILED DESCRIPTION

The present invention, which is directed to a MOSFET having a steepretrograded dopant island that reduces short-channel effects withoutincreasing device leakage, and a method of forming a MOSFET having asteep retrograded dopant island, will now be discussed in greater detailby referring to the drawings that accompany the present application. Inthe accompanying drawings, like and or corresponding elements arereferred to by like reference numbers.

Referring to FIG. 1, illustrating one embodiment of the presentinvention, a MOSFET 5 is provided comprising a steep retrograded dopantisland 10, in which the steep retrograded dopant island 10 issubstantially aligned with the sidewalls of the overlying gate region15. The gate region 15 includes a gate conductor 14, and a gatedielectric 13. Sidewall spacers 60 and offset spacers 11 are positionedadjacent to the gate region 15. The steep retrograded dopant island 10comprises a first conductivity type dopant in a concentration thatreduces the incidence of short-channel effects and is positioned withinthe device to ensure that the dopant concentration of the steepretrograded dopant island 10 does not substantially increase deviceleakage.

The steep retrograded dopant island 10 is positioned underlying thedevice channel 20, in which the device channel 20 has a firstconductivity type dopant having a concentration at least one order ofmagnitude lower than the dopant concentration of the steep retrogradeddopant island 10. The lower dopant concentration of the device channel20 ensures that the charge carriers within the device channel 20 have ahigh mobility.

Regrown Si-containing regions 30 are positioned adjacent to the devicechannel 20 and the steep retrograded dopant island 10. The regrownSi-containing regions 30 comprise source/drain extensions 35 and deepsource/drain regions 40 having a second conductivity type dopant. Thesource/drain extensions 35 abut the device channel 20. The deepsource/drain regions 40 are separated from the steep retrograded dopantisland 10 by a first conductivity type doped portion of the regrownSi-containing material having a doping concentration lower than thesteep retrograded dopant island 10. The portion of the regrownSi-containing material separating the steep retrograded dopant island 10from the deep source/drain regions 40 is hereafter referred to as aleakage inhibiting doped region 45.

When the first conductivity type dopant is an n-type dopant, such asarsenic or phosphorus, the second conductivity type dopant is a p-typedopant such as boron or indium. Conversely, if the first conductivitytype dopant is a p-type dopant, the second conductivity type dopant isan n-type dopant.

In one embodiment of the present invention, the dopant concentration ofthe steep retrograded dopant island 10 ranges from about 5×10¹⁸atoms/cm³ to about 2×10²⁰ atoms/cm³, preferably being about 5×10¹⁹atoms/cm³; the device channel 20 has a dopant concentration ranging fromabout 1×10¹⁸ atoms/cm³ to about 5×10¹⁸ atoms/cm³, preferably being about3×10¹⁸ atoms/cm³; and the leakage inhibiting doped region 45 has adopant concentration ranging from about 1×10¹⁸ atoms/cm³ to about 1×10¹⁹atoms/cm³, preferably being about 5×10¹⁸ atoms/cm³. The source/drainextension regions 35 may have a dopant concentration ranging from about5×10¹⁹ atoms/cm³ to about 5×10²⁰ atoms/cm³, preferably being about2×10²⁰ atoms/cm³; and the deep source/drain regions 40 may have a dopantconcentration ranging from about 1×10²⁰ atoms/cm³ to about 5×10²⁰atoms/cm³ preferably being about 3×10²⁰ atoms/cm³. The method of formingthe MOSFET depicted in FIG. 1 is now described in FIGS. 2-7.

Reference is first made to FIG. 2, which illustrates an initialstructure that can be employed in the present invention including a gatestack 50 atop a layered structure 55. Specifically, the layeredstructure 55 comprises a channel layer 20′ atop a low diffusivity layerof a first conductivity type dopant 10′, wherein the low diffusivitylayer of a first conductivity type dopant 10′ is positioned on asubstrate 52.

The substrate 52 includes, but is not limited to: any semiconductingmaterial such conventional Si-containing materials, GaAs, InAs and otherlike semiconductors. Si-containing materials include, but are notlimited to: Si, bulk Si, single crystal Si, polycrystalline Si, SiGe,amorphous Si, silicon-on-insulator substrates (SOI), SiGe-on-insulator(SGOI), annealed poly Si, and poly Si line structures.

Still referring to FIG. 2, the low diffusivity layer of firstconductivity type dopant 10′ is formed atop the substrate 52 byepitaxial growth or like processes. The first conductivity type dopantmay be a p-type or n-type dopant present in a concentration ranging fromabout 1×10¹⁹ atoms/cm³ to about 1×10²⁰ atoms/cm³. The low diffusivitylayer of first conductivity type dopant 10′ may be doped duringepitaxial growth or it may be doped by ion implantation followinggrowth.

In one embodiment of the present invention, the epitaxially grown lowdiffusivity layer of first conductivity type dopant 10′ has thecomposition Si_(1-x-y)Ge_(x)Z_(y), wherein Z is a diffusion inhibitingdopant, x ranges from about 0.0 to about 0.2, and y ranges from about0.001 to about 0.01. The Ge concentration of the low diffusivity layerof first conductivity type dopant 10′ is selected to produce an internalstress within the low diffusivity layer of first conductivity typedopant 10′. The internal stress is produced by depositing a materiallayer (such as the low diffusivity layer of first conductivity typedopant 10′) having a different energetically favorable lattice dimensionthan the surface on which the material layer is grown (substrate 52),since the lattice dimension of the material layer is strained to matchthe lattice dimension of the surface on which the material layer isgrown. The greater the Ge concentration within the low diffusivity layerof first conductivity type dopant 10′, the greater the differentialbetween the lattice dimensions of the low diffusivity layer of firstconductivity type dopant 10′ and the substrate 52. The epitaxially grownlow diffusivity layer of first conductivity type dopant 10′ may functionas an etch stop during subsequent processing.

The strain produced in the low diffusivity layer of first conductivitytype dopant 10′ is maintained so long as the low diffusivity layer offirst conductivity type dopant 10′ is not grown to a thickness greaterthan its critical thickness. If the material layer is grown to athickness greater than its critical thickness, the material layer willgrow having its energetically favorable lattice dimension that differsfrom the lattice dimension of the surface on which the material layer isgrown and will relax via dislocation formation. Typically, the lowdiffusivity layer of first conductivity type dopant 10′ can be grown toa thickness ranging from about 10 nm to about 50 nm.

The diffusion inhibiting dopant can comprise carbon (C), xenon (Xe),germanium (Ge), krypton (Kr), argon (Ar), nitrogen (N), or combinationsthereof. When producing n-type MOSFETs, the diffusion inhibiting dopantof the low diffusivity layer of first conductivity type dopant 10′ ispreferably carbon present in an concentration from about 1×10¹⁹atoms/cm³ to about 5×10²⁰ atoms/cm³. When producing p-type MOSFETs, thediffusion inhibiting dopant of the low diffusivity layer of firstconductivity type dopant 10′ is preferably xenon present in aconcentration from about 1×10¹⁹ atoms/cm³ to about 5×10²⁰ atoms/cm³.

In another embodiment of the present invention, the low diffusivitylayer of first conductivity type dopant 10′ may be formed by epitaxiallygrowing strained Si_(1-x)Ge_(x) (x ranges from about 0.0 to about 0.2)and then ion implanting the diffusion inhibiting dopant. In thisembodiment, ion implantation of the diffusion inhibiting dopant isfollowed by a thermal anneal process step to remove implant damage.

The channel layer 20′ is epitaxially grown atop the low diffusivitylayer of first conductivity type dopant 10′. The channel layer 20′comprises a Si-containing material and has a thickness ranging fromabout 10 nm to about 20 nm. The channel layer 20′ can be doped with afirst conductivity type dopant during epitaxial growth or via ionimplantation. The dopant concentration o the channel layer 20′preferably ranges from 1×10¹⁷ atoms/cm³ to about 5×10¹⁸ atoms/cm³.

Still referring to FIG. 2, a gate stack 50 is formed atop the layeredstructure 55 using conventional forming processes. The gate stack 50comprises a gate dielectric layer 13′, a gate conductor layer 14′, and agate cap layer 12′.

The gate dielectric layer 13′ may be composed of a nitride, oxynitride,or a combination thereof. The gate dielectric layer is formed usingdeposition techniques, such as chemical vapor deposition (CVD), atomiclayer CVD (ALCVD), pulsed CVD, plasma assisted CVD, sputtering, andchemical solution deposition, or by a thermal growing process, such asoxidation, oxynitridation, nitridation, and/or plasma or radicaltreatment. Suitable examples of oxides that can be employed as the gatedielectric layer include, but are not limited to: SiO₂, Al₂O₃, ZrO₂,HfO₂, Ta₂O₃, TiO₂, perovskite-type oxides and combinations andmulti-layers thereof. The gate dielectric layer 13′ preferably has athickness ranging from about 0.5 nm to about 3.0 nm, preferably beingless than 1.0 nm. The gate dielectric layer 13′ is subsequently etchedto form the gate dielectric.

After gate dielectric layer 13′ has been formed, the gate conductorlayer 14′ is formed atop the gate dielectric layer 13′ by a depositionprocess (such as CVD, plasma-assisted CVD, plating, sputtering and etc.)Gate conductor layer 14′ may comprise any conductive material including,but not limited to: polysilicon; a conductive elemental metal such as W,Cu, Pt, Ag, Au, Ru, Ir, Rh, and Re; alloys that include at least one ofthe aforementioned conductive elemental metals; silicides or nitridesthat include at least one of the above-mentioned conductive elementalmetals; and combinations thereof may be employed. Examples of silicidesthat may be utilized in the gate conductor layer 14′ include CoSi₂ andNiSi. Examples of nitrides that may be utilized in the gate conductorlayer 14′ includes TiN, WN, and TaN.

A highly preferred conductive material employed in the gate conductorlayer 14′ is polysilicon doped with first or second conductivity typedopants. When a polysilicon gate conductor is employed, the polysilicongate conductor is formed by deposition, ion implantation and annealing.The dopant may also be introduced during deposition of the gateconductor layer 14′.

Still referring to FIG. 2, the gate cap layer 12′ is optionally formedatop the gate conductor layer 14′. In a preferred embodiment of thepresent invention, gate cap layer 12′ may be a nitride or oxynitride,with Si₃N₄ being highly preferred. The gate cap layer 12′ can bedeposited using a conventional deposition process including, but notlimited to: chemical vapor deposition, room temperature chemical vapordeposition, or plasma enhanced chemical vapor deposition. The thicknessof the gate cap layer 12′ may range from about 10.0 nm to about 100.0nm.

Referring to FIG. 3, the gate stack 50 is then patterned and etched toform a gate region 15 using deposition, photolithography, and etching.Specifically, a pattern is produced by applying a photoresist to thesurface to be patterned; exposing the photoresist to a pattern ofradiation; and then developing the pattern into the photoresistutilizing a conventional resist developer. Once the patterning of thephotoresist is completed, the sections covered by the photoresist areprotected, while the exposed regions are removed using a selectiveetching process that removes the unprotected regions of the gate stack50. Preferably, this etch process has a high selectivity for removingthe material of the gate cap layer 12′, the gate conductor layer 14′ andthe gate dielectric layer 13′ without substantially etching thepatterned photoresist and the channel layer 20′ of the stacked structure55. Following etching, the patterned photoresist is removed using achemical strip. The resultant gate region 15 includes a gate cap 12 atopa gate conductor 14, wherein the gate conductor 14 is positioned atop agate dielectric 13.

In a next process step, thin sidewall spacers 60 are formed abutting thegate region 15. Preferably, the thin sidewall spacer 60 is a nitride,such as Si₃N₄. The thin sidewall spacer width ranges from about 1 nm toabout 20 nm, preferably being about 3 nm. Forming processes such asdeposition or thermal growing may produce the thin sidewall spacer 60.Preferably, the thin sidewall spacer 60 is formed by a depositionprocess such as, for example, chemical vapor deposition (CVD),low-pressure chemical vapor deposition (LPCVD), rapid thermal chemicalvapor deposition (RTCVD), or plasma enhanced chemical vapor deposition(PECVD) in combination with a directional reactive ion etch.

Referring to FIG. 4, in a next process step the device channel 20 isformed by a directional etch process, such as reactive ion etch (RIE),in which the overlying gate region 15 functions as an etch mask. In apreferred embodiment, the directional etch process is selective toremoving the exposed portions of the device channel layer 20 withoutsubstantially etching the gate cap 12 or the low diffusivity layer offirst conductivity dopant 10′.

In one embodiment of the present invention and following device channel20 etching, the low diffusivity layer of a first conductivity dopant 10′can be doped by an angled ion implantation 53 to provide a non-uniformlateral doping profile underlying the device channel. The angled ionimplantation 53 may be referred to a halo implantation. NFET devices aretypically implanted with a p-type halo implant and pFET devices aretypically implanted with an n-type halo implant.

Referring to FIG. 5, in a next process step the exposed portion of thelow diffusivity layer of a first conductivity type dopant and a portionof the substrate 52 are etched by a timed directional etch. Theremaining portion of the low diffusivity layer of first conductivitytype dopant provides a steep retrograded dopant island 10 havingsidewalls that are substantially aligned with the sidewalls of theoverlying gate region 15. The etch process is timed to expose a recessedsurface 65 of the substrate 52. The substrate surface 65 is recessed toavoid positioning defects that are formed during subsequent epitaxialgrowth of the regrown Si-containing material atop the recessed surface65 of the substrate 52 too close to the interface of the subsequentlyformed deep source/drain regions and the channel 20. Typically, therecessed surface 65 of the substrate 52 is recessed about 20 nm to about30 nm from the original upper surface of the substrate 52 for asilicon-on-insulator (SOI) substrate device and about 100 nm to about300 nm from the original upper surface of the substrate 52 for a bulkSi-containing substrate device. Following etch, the gate cap 12 may beremoved from the surface of the gate conductor 14.

Referring to FIG. 6, a regrown Si-containing material 30 is thenepitaxially formed atop the recessed surface 65 of the substrate 52. Theregrown Si-containing material 30 may comprise Si, SiGe, or Si:C(silicon doped with carbon).

In one embodiment of the present invention, the regrown Si-containingmaterial 30 transfers a compressive stress into the device channel 20that increases device performance in p-type MOSFETS. In this embodiment,the regrown Si-containing material 30 comprises epitaxially grown SiGe.The Ge concentration in this embodiment may range from about 5% to about30%.

Epitaxially growing the larger lattice dimension SiGe atop the smallerlattice dimension of the substrate 52 creates an internal compressivestress. The SiGe regrown Si-containing material 30 transfers theinternal compressive stress into the device channel 20. Therefore, thedevice channel 20 is strained to provide strained-Si device improvementsfor p-type MOSFET devices, in which the compressive strain transferredfrom the regrown Si-containing material 30 increases the carriermobility for p-type channels.

In another embodiment of the present invention, the regrownSi-containing material 30 transfers a tensile stress into the devicechannel 20 that increases device performance in n-type MOSFETS. In thisembodiment, the regrown Si-containing material 30 comprises epitaxiallygrown Si:C, in which increasing the C concentration of the regrownSi-containing material 30 decrease the energetically favorable latticedimension of the regrown Si-containing material 30. The C concentrationin this embodiment may range from about 0.1% to about 2%.

Epitaxially growing the smaller lattice dimension Si:C atop the largerlattice dimension of the substrate creates an internal tensile stress.The Si:C regrown Si-containing material 30 transfers the internaltensile stress into the device channel 20. Therefore, the device channel20 is strained to provide strained-Si device improvements for n-typeMOSFET devices, in which the tensile strain transferred from the regrownSi-containing material 30 increases the carrier mobility for n-typechannels.

Still referring to FIG. 6, source/drain extension regions 35 are thenformed in regrown Si-containing material 30 and partially extend underthe gate region 15. Source/drain extension regions 35 are formed via ionimplantation and comprise a combination of normally incident and angledimplants of second conductivity type dopants to form the desired gradingin the extensions. P-type MOSFET devices are produced by doping thesource/drain extension regions 35 with elements from group III of thePeriodic Table of Elements. N-type MOSFET devices are produced withinSi-containing substrates by doping the source/drain extension regions 7with elements from group V of the Periodic Table of Elements.

When the first conductivity type dopant utilized in the device channel20 and the steep retrograded dopant island 10 is a p-type dopant, thesecond conductivity type dopant used in the source/drain extensionregions 35 is an n-type dopant. When the first conductivity type dopantutilized in the device channel 20 and the steep retrograded dopantisland 10 is an n-type dopant, the second conductivity type dopant usedin the source/drain extension regions 35 is a p-type dopant.

Halo regions may also be formed beneath the source/drain extensionregions 35 using an angled ion implantation and a dopant having aconductivity type opposite the source/drain extension regions 35.

Referring to FIG. 7, following source/drain extension region 35implants, an offset spacer 11 is formed abutting the sidewall spacer 60.The offset spacer 11 is formed using conventional deposition and etchingprocesses that are well known in the art and preferably comprises anitride, such as Si₃N₄. The offset spacer 11 has a greater width thanthe sidewall spacer 60. The offset spacer 11 width ranges from about 10nm to about 200 nm.

Following offset spacer 11 formation, a higher energy ion implant of asecond conductivity type dopant is conducted to form deep source/drainregions 40. These implants are conducted at a higher energy and higherconcentration of second conductivity type dopant than the source/drainextension region 35 implant. The dopant concentration of the deepsource/drain regions 40 ranges from about 1×10²⁰ atoms/cm³ to about5×10²⁰ atoms/cm³. The deep source/drain regions 40 are typically dopedwith a dopant type consistent with the source/drain extension regions35. For example, p-type source/drain regions 40 are typically doped withboron at a concentration of about 1×10¹⁵ atoms/cm³ to about 5×10¹⁵atoms/cm³ and implant energy of about 1 keV to about 10 keV. N-typesource/drain regions 40 are typically doped with arsenic at aconcentration of about 1×10¹⁵ atoms/cm³ to about 5×10¹⁵ atoms/cm³ andimplant energy of about 5 keV to about 40 keV.

The width of the offset spacer 11 and the energy of the implant to formthe deep source/drain regions 40 ensure that the deep source/drainregions 40 are separated from the steep retrograded dopant island 101 bya leakage inhibiting doped region 45 of a first conductivity type dopantand a dopant concentration ranging from about 1×10¹⁸ atoms/cm³ to about1×10²⁰ atoms/cm³.

Following deep source/drain region 40 formation, the deep source/drainregions 40 and gate region 15 are activated by activation annealingusing conventional processes such as, but not limited to: rapid thermalannealing, furnace annealing, flash lamp annealing or laser annealing.Activation anneal is conducted at a temperature ranging from about 850°C. to about 1350° C.

While the present invention has been particularly shown and describedwith respect to preferred embodiments thereof, it will be understood bythose skilled in the art that the foregoing and other changes in formsand details may be made without departing from the spirit and scope ofthe present invention. It is therefore intended that the presentinvention not be limited to the exact forms and details described andillustrated, but fall within the scope of the appended claims.

1. A semiconducting device comprising: a gate region positioned on achannel portion of a substrate that comprises a first semiconductormaterial, wherein said channel portion of said substrate is positionedatop a first conductivity type retrograded dopant island having a dopantof said first conductivity type at a first dopant concentration andvertically abutting said first semiconductor material, wherein saidfirst conductivity type retrograded dopant island comprises Si; and apair of Si-containing material portions, each comprising a secondsemiconductor material having a different lattice dimension than saidfirst semiconductor material and including a first conductivity typedoped portion, said Si-containing material portions comprise one ofepitaxial Si:C and epitaxial SiGe, and said Si-containing materialportions comprise at least one semiconductor material not included insaid first conductivity type retrograded dopant island, wherein each ofsaid first conductivity type doped portion has a dopant of said firstconductivity type at a second dopant concentration lower than said firstdopant concentration, wherein sidewalls of said first conductivity typeretrograded dopant island laterally abut each of said first conductivitytype doped portions and are vertically aligned to sidewalls of said gateregion.
 2. The semiconducting device of claim 1 wherein said channelportion of said substrate comprises a thickness ranging from about 10 nmto about 20 nm and a channel length of approximately 100 nm or less. 3.The semiconducting device of claim 1 wherein said first conductivityretrograded dopant island comprises Si_(1-x-y) Ge_(x)Z_(y), wherein Zcomprises a diffusion limiting dopant.
 4. The semiconducting device ofclaim 3 wherein said first conductivity dopant of said firstconductivity retrograded dopant island is an n-type dopant and Z isselected from the group consisting of xenon, carbon, germanium, krypton,argon, nitrogen, and combinations thereof.
 5. The semiconductor deviceof claim 4 wherein Z is selected from the group consisting of xenon,carbon, krypton, argon, nitrogen, and combinations thereof.
 6. Thesemiconductor device of claim 5 wherein Z is selected from the groupconsisting of xenon, krypton, argon, nitrogen, and combinations thereof.7. The semiconducting device of claim 3 wherein said first conductivitydopant of said first conductivity retrograded dopant island is a p-typedopant and Z is selected from the group consisting of xenon, carbon,germanium, krypton, argon, nitrogen, or combinations thereof.
 8. Thesemiconducting device of claim 1 wherein said first conductivityretrograded dopant island has said first dopant concentration at leastan order of magnitude greater than said channel portion.
 9. Thesemiconductor device of claim 1 wherein each of said Si-containingmaterial portions includes a source/drain extension region having adopant of a second conductivity type and a deep source/drain regionhaving a dopant of said second conductivity type.
 10. The semiconductordevice of claim 9 wherein said source/drain extension regions arevertically aligned to said sidewalls of said gate region.
 11. Thesemiconductor device of claim 10 wherein said source/drain extensionregions directly contact said first conductivity type retrograded dopantisland.
 12. The semiconductor device of claim 1 further comprising anoffset spacer having sidewalls that abut said sidewalls of said gateregion, and wherein said sidewalls of said first conductivity typeretrograded dopant island are vertical sidewalls.
 13. The integratedcircuit of claim 1 wherein sidewalls of said pair of Si-containingmaterial portions laterally abut said first semiconductor material insaid semiconductor substrate.
 14. A semiconducting device comprising: agate region positioned on a channel portion of a substrate thatcomprises a first semiconductor material, wherein said channel portionof said substrate is positioned atop a first conductivity typeretrograded dopant island and between a set of second conductivity typedoped regions, wherein said first conductivity type retrograded dopantisland has a dopant of said first conductivity type at a first dopantconcentration and vertically abutting said first semiconductor material;and a pair of Si-containing material portions, each comprising a secondsemiconductor material having a different lattice dimension than saidfirst semiconductor material and including a first conductivity typedoped portion, wherein each of said first conductivity type dopedportion has a dopant of said first conductivity type at a second dopantconcentration lower than said first dopant concentration, whereinsidewalls of said first conductivity type retrograded dopant islandlaterally abut each of said first conductivity type doped portions andare vertically aligned to sidewalls of said gate region, wherein saidset of second conductivity type doped regions comprise SiGe and saidchannel portion further comprises an internal compressive stress.
 15. Asemiconducting device comprising: a gate region positioned on a channelportion of a substrate that comprises a first semiconductor material,wherein said channel portion of said substrate is positioned atop afirst conductivity type retrograded dopant island and between a set ofsecond conductivity type doped regions, wherein said first conductivitytype retrograded dopant island has a dopant of said first conductivitytype at a first dopant concentration and vertically abutting said firstsemiconductor material; and a pair of Si-containing material portions,each comprising a second semiconductor material having a differentlattice dimension than said first semiconductor material and including afirst conductivity type doped portion, wherein each of said firstconductivity type doped portion has a dopant of said first conductivitytype at a second dopant concentration lower than said first dopantconcentration, wherein sidewalls of said first conductivity typeretrograded dopant island laterally abut each of said first conductivitytype doped portions and are vertically aligned to sidewalls of said gateregion, wherein said set of second conductivity type doped regionscomprise Si:C and said channel portion further comprises an internaltensile stress.